Statements like "heat treating" and "mild steel" should not be used together. Mild steel is not a heat treatable material. While a weld will be harder than the base material, it is no where near as hard as you might think it is.
If you can't drill through it, your doing it wrong. Simple as that really.
If you can't drill through it, your doing it wrong. Simple as that really.